247 ipc and history results

Electronics Forum: ipc and history (Page 6 of 25)

board stretch and IPC -D-300G

Electronics Forum | Mon Nov 12 17:12:40 EST 2001 | slthomas

Thanks, Dave. Three courtesy cheers for specifications written to reflect the capabilities of the part suppliers, even if they fail to meet the purchaser's (not unreasonable) process req'ts. In the meantime, I'm sure my stencil guy would be more

V-scoring design and equipment questions

Electronics Forum | Mon Jun 12 18:44:30 EDT 2006 | muse95

OK, Pete, I just looked all through IPC-A-600G. Saw no mention of scoring anywhere. Please provide specific section number info. Thanks By the way, Chris, thank you for the information - that is really interesting stuff. Would you be willing to a

Re: BGA and Land Patterns

Electronics Forum | Wed Apr 28 14:41:45 EDT 1999 | Bob Willis

| | What is the current spec for sizing PCB pads for a land grid array? How about for a ball grid array? Are there industry spec's I can reference? | | | | Thanks, | | | | Frank | | | Frank, | Refer to the device manufacturers. they are going t

Bow and Twist of PCB's

Electronics Forum | Wed Aug 19 05:00:56 EDT 1998 | Tom Blum

Hi there, I'm actually facing a lot of trouble with PCB's presenting up to 3mm of bow /twist at reception i.e. before assembly. The PCB size is 220 by 230mm. The boards are to be assembeled SMD double sides with 05.mm pitch on both sides. In order to

Pick and Place Machine Validation

Electronics Forum | Mon Mar 28 22:29:42 EST 2005 | msivigny

Appreciate the feedback SMTUser & link referral PeteC! Late 2004, EAGLE-EYED ONE changed its name to CeTaQ Americas. Still the same business, people and quality products and services. Changed for global synergy with our German parent and in support o

Solder beads and wave soldering

Electronics Forum | Thu Jul 06 03:03:56 EDT 2006 | ronalds

Thank you all for your input. The MF300S Multicore flux is rated for lead free. There is not much dross or contamination. We are using nitrogen. I've tested the boards with the curing test of IPC-TM-650. I think you're all right about the preheat.

Wave Cassettes and Heat convection

Electronics Forum | Mon Jan 15 11:41:56 EST 2007 | davef

Questions are: * Does the component take solder when you dip it in the solder pot to test the solderability of the leads? * Can you get full barrel fill when wave soldering a bare board? * Is your flux reaching the top of the board through the hole b

board stretch and IPC -D-300G

Electronics Forum | Mon Nov 12 16:14:47 EST 2001 | davef

Yes!!! How can we assemble boards with 20 pitch when we allow 0.008� error to the master art? Excellent question!!! IPC-D-300G has nothing to do with assembler requirements. It is written by and for fabricators, so that they can be comfortable.

Fuji Pick and Place Machines

Electronics Forum | Sat Jun 05 08:18:03 EDT 2004 | vinitverma

Hi Grant, If you're really looking for speed, I'm sure you're looking for another machine for doing the QFPs, BGAs stuff etc. In that even, why not have a look at the long proven Assembleon FCM machine!! It is a totally different concept with UNMATC

wave soldering and solder bridge

Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef

I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,